Gelince Haber VerPETG HF is a fully optimized PETG filament designed specifically for high-speed printing. With a default printing speed that is twice as fast as standard PETG filaments, PETG HF takes your printing efficiency to new heights.
It effectively addresses common issues such as oozing and clumping associated with regular PETG, ensuring smoother and more reliable prints. The new matte finish not only enhances the aesthetic by smoothing out uneven gloss during speed transitions but also provides a consistently uniform look.
Offering greater durability and toughness than PLA, PETG HF is the ideal choice for creating long-lasting items with an improved finish and faster production times.
* Thank Adrian Luben (Social Handle: @Marsgizmo) for creating this video.
Twice as fast as standard PETG*, PETG HF significantly boosts your productivity without compromising the quality of your prints.
* The speed of PETG HF can be twice as fast compared to regular PETG, but achieving this speed is highly dependant on model size and geometry.
PETG HF excels in printability among PETG filaments with its higher adaptability for printers and printing settings, achieving ideal print results without fine-tuning parameters. Thanks to advanced formula optimization, PETG HF bids farewell to oozing and clumping, ensuring smoother prints with crisp details.
PETG HF provides a smooth texture and consistent gloss at any printing speed, ensuring uniformity and sharp details in every print.
PETG HF maintains the inherent strengths of regular PETG, providing superior resistance to water, UV, and temperatures. Tougher and more durable than PLA, with higher temperature resistance, it's the perfect choice for printing outdoor items such as planter pots, bird cages, watering cans, and automotive parts. Additionally, it's ideal for outdoor toys that require long-term exposure and the ability to withstand impacts, collisions, and falls.
| Recommended | Not Recommended | |
| Build Plate | Smooth PEI Plate,Textured PEI Plate | Cool Plate |
| Hotend | All Size / Material | / |
| Glue | Bambu Liquid Glue Glue Stick |
/ |
| Color | Hex Code | Display |
| Yellow | #FFD00B | |
| Orange | #F75403 | |
| Green | #00AE42 | |
| Red | #EB3A3A | |
| Blue | #002E96 | |
| Black | #000000 | |
| White | #FFFFFF | |
| Gray | #ADB1B2 |
Learn more different filaments comparison on Bambu Filament Guide >>
| PLA Basic |
PETG HF
|
PETG Basic | |
| Printing Speed* | ~ 300 mm/s |
~ 300 mm/s
|
~ 200 mm/s |
| Preset Printing Speed* | 258 mm/s |
258 mm/s
|
172 mm/s |
| Strength (Bending Strength - XY) | 76 MPa |
64 MPa
|
65 MPa |
| Stiffness (Bending Modulus - XY) | 2750 MPa |
2050 MPa
|
1670 MPa |
| Layer Strength (Bending Strength - Z) | 59 MPa |
48 MPa
|
48 MPa |
| Layer Adhesion (Impact Strength - Z) | 13.8 kJ/m² |
10.6 kJ/m²
|
13.6 kJ/m² |
| Toughness (Impact Strength - XY) | 26.6 kJ/m² |
31.5 kJ/m²
|
52.7 kJ/m² |
| Heat Resistance (HDT, 0.45 MPa) | 57 °C |
69 °C
|
69 °C |
1. Maximum Printing Speed* refers to the highest speed achievable by the filament while maintaining high print quality, given an appropriate increase in nozzle temperature.
2. Preset Maximum Printing Speed* refers to the highest speed achievable with default settings, ensuring top printing quality in most environments.
Settings: Bambu Lab X1-Carbon, 0.4 mm nozzle, 0.2 mm layer height
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 65 °C, 8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 230 - 260 °C |
| Bed Temperature (with Glue) | 65 - 75 °C |
| Printing Speed | < 300 mm/s |
| Physical Properties | |
| Density | 1.28 g/cm³ |
| Vicat Softening Temperature | 70 °C |
| Heat Deflection Temperature | 69 °C |
| Melting Temperature | 214 °C |
| Melt Index | 28.2 ± 2.7 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 34 ± 4 MPa |
| Breaking Elongation Rate | 8.6 ± 1.2 % |
| Bending Modulus | 2050 ± 120 MPa |
| Bending Strength | 64 ± 3 MPa |
| Impact Strength | 31.5 ± 2.2 kJ/m² |
Dry out before use for higher printing quality. PETG HF must be dried before use and remain moisture-free during the printing process, especially for longer print times (over 6 hours).
Drying conditions: 65℃ for 8 h in the Blast Drying Oven; 75 - 85℃ for 12 h in the X1 Series Heatbed. For more details please refer to: Filament Drying Recommendations on WIKI. Please note that the spool can withstand the higher temperature for drying on the heatbed.